Rongsheng Refractory Brick Factory Producing Clay Refractory Brick for High Temperature Kiln Lining High Alumina Brick Complete Specifications
Price section
Price from:
4,702,060 so'm
Specifications
Clay fire-resistant bricks
Not actual price, please consult customer service
Guaranteed delivery time
If we are 45 days late, you will receive your order for free. More details
Always in touch with you
We will answer any questions every day.
Secure payment in a convenient way
We will accept payment by any card
BNPL available
About the product
Characteristic
- Material
Material
- Origin
Origin
- Product name
Product name
- Thermal conductivity
Consult customer service
- Fire resistance temperature
1580-1700
- Pressure resistance
Consult customer service
- Brand
Brand
- Model
Complete models support customization
- Is it imported?
Is it imported?
- Is it dangerous chemicals?
Is it imported?
- Adapt to the kiln
Adapt to the kiln
Description
提供定制、样品、窑炉方案：13298319677
提供定制、样品、窑炉解决方案：13298319677
高铝砖是耐火材料的一种三氧化二铝（Al2O3）含量高于48%的硅酸铝质耐火材料制品。
Al2O3含量越高，表面颜色越白。
由矾土或其他氧化铝含量较高的原料经成型和煅烧而成。热稳定性高，耐火度高。抗渣性较好，用于砌筑炼钢电炉、玻璃熔炉、水泥回转炉等的衬里。
a、耐火度
高铝砖的耐火度比粘土砖和半硅砖的耐火度都要高，属于高品质耐火材料。
b、荷重软化温度
因为高铝制品中Al2O3高，杂质量少，形成易熔的玻璃体少，所以荷重软化温度高。
c、抗渣性
高铝砖中Al2O3较多，接近于中性耐火材料，能抵抗酸性渣和碱性渣的侵蚀。
提供定制、样品、窑炉解决方案：13298319677
粘土耐火砖
|
项目 |
指标 |
||
|
PN-42 |
PN-40 |
PN-35 |
|
|
Al2O3 % |
≥42 |
≥40 |
≥35 |
|
Fe2O3 % |
≤2.0 |
≤2.0 |
≤2.5 |
|
显气孔率 % |
≤20 |
≤24 |
≤26 |
|
体积密度 g/cm3 |
2.1~2.25 |
2.05~2.2 |
1.95~2.1 |
|
常温耐压强度 MPa |
≥45 |
≥35 |
≥30 |
|
0.2MPa荷重软化开始温度 ℃ |
≥1400 |
≥1350 |
≥1320 |
|
加热永久线变化 % |
-0.4~0.1 1400℃×2h |
-0.4~0.1 1350℃×2h |
-0.4~0.1 1300℃×2h |
高铝砖指标
|
项目 |
指标 |
|||||
|
LZ-80 |
LZ-75 |
LZ-70 |
LZ-65 |
LZ-55 |
LZ-48 |
|
|
Al2O3 % |
≥80 |
≥75 |
≥70 |
≥65 |
≥55 |
≥48 |
|
显气孔率 % |
≤21 |
≤24 |
≤24 |
≤24 |
≤22 |
≤22 |
|
常温耐压强度 MPa |
≥70 |
≥60 |
≥55 |
≥50 |
≥45 |
≥40 |
|
0.2MPa荷重软化开始温度 ℃ |
≥1530 |
≥1520 |
≥1510 |
≥1500 |
≥1450 |
≥1420 |
|
加热永久线变化 % |
1500℃×2h -0.4~0.2 |
1450℃×2h -0.4~0.1 |
||||
指标仅供展示，下单请联系客服确认价格、运费，未经客服同意付款无法发货。
Characters
Properties
- Material
Material
- Origin
Origin
- Product name
Product name
- Thermal conductivity
Consult customer service
Description
提供定制、样品、窑炉方案：13298319677
提供定制、样品、窑炉解决方案：13298319677
高铝砖是耐火材料的一种三氧化二铝（Al2O3）含量高于48%的硅酸铝质耐火材料制品。
Al2O3含量越高，表面颜色越白。
由矾土或其他氧化铝含量较高的原料经成型和煅烧而成。热稳定性高，耐火度高。抗渣性较好，用于砌筑炼钢电炉、玻璃熔炉、水泥回转炉等的衬里。
a、耐火度
高铝砖的耐火度比粘土砖和半硅砖的耐火度都要高，属于高品质耐火材料。
b、荷重软化温度
因为高铝制品中Al2O3高，杂质量少，形成易熔的玻璃体少，所以荷重软化温度高。
c、抗渣性
高铝砖中Al2O3较多，接近于中性耐火材料，能抵抗酸性渣和碱性渣的侵蚀。
提供定制、样品、窑炉解决方案：13298319677
粘土耐火砖
|
项目 |
指标 |
||
|
PN-42 |
PN-40 |
PN-35 |
|
|
Al2O3 % |
≥42 |
≥40 |
≥35 |
|
Fe2O3 % |
≤2.0 |
≤2.0 |
≤2.5 |
|
显气孔率 % |
≤20 |
≤24 |
≤26 |
|
体积密度 g/cm3 |
2.1~2.25 |
2.05~2.2 |
1.95~2.1 |
|
常温耐压强度 MPa |
≥45 |
≥35 |
≥30 |
|
0.2MPa荷重软化开始温度 ℃ |
≥1400 |
≥1350 |
≥1320 |
|
加热永久线变化 % |
-0.4~0.1 1400℃×2h |
-0.4~0.1 1350℃×2h |
-0.4~0.1 1300℃×2h |
高铝砖指标
|
项目 |
指标 |
|||||
|
LZ-80 |
LZ-75 |
LZ-70 |
LZ-65 |
LZ-55 |
LZ-48 |
|
|
Al2O3 % |
≥80 |
≥75 |
≥70 |
≥65 |
≥55 |
≥48 |
|
显气孔率 % |
≤21 |
≤24 |
≤24 |
≤24 |
≤22 |
≤22 |
|
常温耐压强度 MPa |
≥70 |
≥60 |
≥55 |
≥50 |
≥45 |
≥40 |
|
0.2MPa荷重软化开始温度 ℃ |
≥1530 |
≥1520 |
≥1510 |
≥1500 |
≥1450 |
≥1420 |
|
加热永久线变化 % |
1500℃×2h -0.4~0.2 |
1450℃×2h -0.4~0.1 |
||||
指标仅供展示，下单请联系客服确认价格、运费，未经客服同意付款无法发货。